Vulcanizable blend of bromine-containing fluoropolymer and fluorosilicone gums

ABSTRACT

A blend of (a) 90 to 20 parts fluoropolymer gum of 60 to 85 mol percent vinylidene fluoride, 10 to 40 mol percent of hexafluoropropene and 0.15 to 3 mol percent bromine-containing olefin, and (b) 10 to 80 parts fluorosilicone gum is provided which can be vulcanized in presence of free-radical initiators to produce elastomeric vulcanizates with desired balance of chemical solvent or fluid resistance, high temperature stability, and low temperature flexibility.

This invention relates to vulcanizable blends of fluoropolymer and fluorosilicone gums and to shaped articles made of vulcanized elastomers of such blends.

Fluoroelastomers, particularly the copolymers of vinylidene fluoride (commonly abbreviated as VF₂) with other ethylenically unsaturated halogenated monomers, such as C₃ F₆ (hexafluoropropene, commonly abbreviated as HFP), C₃ F₅ H, C₂ F₃ Cl, and C₂ F₄, have become the polymers of choice for high temperature applications, such as seals, gaskets, and linings, especially when shaped articles thereof are subject to exposure to aggressive or harsh environments, such as solvents, lubricants, and oxidizing or reducing conditions. Such fluoroelastomers in general can be compounded and cured to have high tensile strength, good tear resistance, and low compression set.

The major drawback to many applications of shaped articles made of such fluoroelastomers has been their inability to satisfactorily function at low temperatures. At temperatures only slightly below 0° C., the articles become stiff and fail to perform satisfactorily. For example, many automotive applications require useful performance at -30° C., preferably -40° C., and the present commercially available fluoroelastomers qualify for use only in a few very special applications where low temperatures do not materially affect the performance of the elastomers. Recent employment of required pollution control devices on automobile engines has resulted in higher and higher temperatures in the vicinity of the engines, and the need for materials that can operate for extended periods at elevated temperatures is becoming even more imperative.

Conventional cured fluoroelastomers with a mol percent composition of VF₂ :HFP of 70-85:15-30 or a mol percent composition of VF₂ :HFP:C₂ F₄ of 56-68:12-24:18-22 have low temperature retraction values (TR₁₀) of -17° to -18° C. and use temperatures (the lowest temperature at which an elastomeric seal is operable) of no more than 10° C. lower, depending somewhat upon the use. Minor changes in monomer composition can lower the TR₁₀ values slightly; for example, a commercial fluoroelastomer having a mol percent composition VF₂ :HFP:C₂ F₄ of 57-61:27-31:10-14 provides a TR₁₀ value of about -19° C. Another commercial fluoroelastomer having the composition VF₂ :C₂ F₄ :C₂ F₃ OCF₃ provides a TR₁₀ value of -28° C.; its cost is so high that it has only minor usage compared to present commercial fluoroelastomer.

At about the same time as fluoroelastomers were developed, another new type of elastomer became commercially important--the polysiloxanes or silicones. Shaped articles of these polymers perform at high temperatures, but additionally they have good physical properties at extremely low temperatures, functioning satisfactorily as low as -60° C. or below. Unfortunately the solvent resistance of the silicones is quite poor, and performance in the presence of solvents, fuels, and lubricants is quite limited. The polyfluorosilicones, particularly those containing trifluoropropyl radicals attached to the silicon atoms, have somewhat improved solvent resistance, but are still inadequate where both high temperature and aggressive solvent environments are encountered.

Over the years a variety of attempts have been made to combine the two classes of polymers, but with very limited success. Publications of such attempts include U.S. Pat. No. 3,415,900 (Robb) which discloses vulcanizing a compounded mixture comprising a fluoroelastomer, such as a VF₂ /HFP copolymer, a silicone rubber, such as phenyl, methyl, or vinyl siloxane rubbers and their halo-substituted derivatives, and a peroxy vulcanization catalyst. U.S. Pat. No. 3,538,028 (Morgan) discloses vulcanizing a mixture comprising a VF₂ /HFP copolymer, a silicone gum such as a copolymer of dimethyl siloxane and trifluoropropylsiloxane, amine accelerators, and peroxy catalysts. U.S. Pat. No. 3,969,308 (Penneck) discloses blending a polymer, such as VF₂ /HFP copolymer, a silicone polymer such as 3,3,3-trifluoropropyl methyl siloxane, a silane-treated inorganic silicon compound containing Si-O-Si groups, and a peroxy initiator. U.S. Pat. No. 4,028,431 (Futami et al) discloses a blend consisting essentially of a fluorine containing ethylene copolymer, a silicone rubber and/or fluorine containing copolymer such as VF₂ /HFP copolymer, and peroxide. British Patent Specification No. 1,284,081 (Raychem Ltd.) discloses a blend of fluorohydrocarbon polymer such as a VF₂ /HFP copolymer, and a silicone polymer such as 3,3,3-trifluoropropyl methyl siloxane. Technical Report AFML-TR-74-92, September, 1974, of the U.S. Air Force Materials Laboratory discloses peroxide-curable blends of an experimental fluorocarbon elastomer described as LD-487 and a fluorosilicone gum sold under the trademark "Silastic" LS-420.

As the foregoing publications show, the customary approach has been to blend the two elastomer gums together and to vulcanize the mixture, sometimes each gum stock having its own curing system and at times a single curing system "suitable" for both. In no case has a commercially satisfactory "cocured" product been obtained suitable for commercial use with a combination of high temperature stability, low temperature flexibility, and solvent resistance.

Problems arise primarily because the two classes of polymers are generally incompatible and have different curing characteristics. The silicones are customarily cured by means of organic peroxides at preset temperatures of 100°-150° C. Fluoroelastomers are usually cured by amines or by diphenol systems, both of which systems are generally incompatible with silicone cures. Peroxide cures have been used for fluoroelastomers in the past and attempts have been made to cocure mixtures of silicones and fluoroelastomers with peroxide initiators. None of the attempts have resulted in properties good enough for practical use.

According to this invention, there is provided a novel blend of certain fluoropolymer gums with fluorosilicone gums, both of which gums cure in the presence of free-radical initiators under vulcanization conditions to produce an elastomeric vulcanizate with a desired balance of chemical and solvent or fluid resistance, high temperature stability, and low temperature utility.

Although blending the fluoropolymer gum with a small amount of fluorosilicone gum (say about 5 parts or less) provides improvement in TR₁₀ value over that provided by the fluoropolymer gum per se, the advantages of such improvement will be outweighed by cost disadvantages in preparing blends with such small amount of fluorosilicone gum. Thus, the fluoropolymer gum:fluorosilicone gum weight ratio in the novel blends of this invention will be in the range of 90:10 to 20:80. Low amounts of the fluoropolymer gum component in these blends usually are difficult to homogeneously disperse in the correspondingly high amounts of the relatively softer fluorosilicone gum; some types of commercial reinforcing fillers assist in overcoming this difficulty and the vulcanizates prepared from such blends have mechanical properties and thermal stabilities which are superior to those prepared from the unblended fluorosilicone gum. The more preferred blends of this invention for many applications will have a fluoropolymer:fluorosilicone weight ratio in the range of 90:10 to 60:40.

The fluoropolymers used in this invention are copolymers whose interpolymerized units consist essentially of 60 to 85 mol percent of units derived from vinylidene fluoride, 10 to 40 mol percent of units derived from hexafluoropropene, and 0.15 to 3 mol percent of units derived from one or more bromine-containing copolymerizable olefins, based on the total moles of interpolymerized units. While up to 10 mol percent of units derived from other highly fluorinated olefins, such as trifluoroethylene, trifluorochloroethylene and tetrafluoroethylene, can be included in the copolymer, the resulting vulcanized products made from blends containing such highly fluorinated olefins tend to have surprisingly poorer physical properties and low temperature performance as compared to blends made with the fluoropolymers which are free of said other fluorinated olefins. Similarly, blends containing copolymerizable fluorinated monomers with lower levels of fluorine, such as vinyl fluoride, tend to give vulcanizates with less resistance to solvents and aggressive chemicals. The first three named monomers are the sole essential comonomers of the fluoropolymer used in this invention, i.e., the fluoropolymer components consists essentially of interpolymerized units derived from VF₂, HFP, and bromine-containing olefin. The preferred fluoropolymers are those whose interpolymerized units consist of 65 to 82 mol percent of units derived from VF₂, 17 to 35 mol percent of units derived from HFP, and 0.2 to 0.6 mol percent of units derived from bromine-containing olefin.

The copolymerizable bromine-containing olefins used in this invention include terminally unsaturated olefins of two to four carbon atoms in which at least one hydrogen atom is substituted by bromine and optionally one or more of the remaining hydrogen atoms have been replaced by fluorine. Such olefins include 4-bromo-perfluorobutene-1, vinyl bromide, pentafluoroallyl bromide, 4-bromo-difluorobutene-1, 2-bromoheptafluorobutene-1, 3-bromoheptafluorobutene-1, difluoroallyl bromide, bromotrifluoroethylene and 1-bromo-2,2-difluoroethylene, the latter two being the preferred bromine-containing olefins to be used in preparing the fluoropolymer component.

A number of the fluoropolymers useful as blend components in this invention are known. The fluoropolymers can be prepared by known polymerization techniques, for example that described in U.S. Pat. No. 4,035,565 (Apotheker et al). Briefly, the fluoropolymers are prepared by charging a stainless steel pressure reactor with reaction diluent, pH buffer, emulsifier, initiator, and the comonomers; carrying out the emulsion polymerization of the charge at constant elevated temperature and pressure, with agitation; coagulating the resulting latex; and filtering, washing, and drying the resulting fluoropolymer gum.

As a representative example, a VF₂ /HFP/bromodifluoroethylene fluoropolymer gum can be prepared according to the above procedure by charging the following ingredients, in order, to a one-gallon, stainless steel, stirred reactor:

Deionized water: 3670 g

K₂ HPO₄ : 16

Perfluorooctanoic acid: 15.7

K₂ S₂ O₈ : 4

HFP: 28

Monomer blend: 1431

VF₂ : 78.3 mol%

HFP: 21.4 mol%

1-Bromo-2,2-difluoroethylene: 0.3 mol%

The reaction mixture is polymerized at 68° C. and 1.3 MPa with an agitation speed of 700 rpm for about 10 hours. A portion of resulting latex (3200 g) is added dropwise to an aqueous solution containing 1200 g deionized water, 18 g CaCl₂, and 21 g H₃ PO₄. After coagulation is complete, the raw gum is washed 5 times with hot deionized water (about 60° C.). Excess water is removed, and the raw gum and is dried overnight at 116° C.

The preferred fluorosilicone gums to be blended with the above-described fluoropolymer gums are poly(trifluoropropyl)methylsiloxanes which have a linear backbone of Si-O-repeating units with principally trifluoropropyl radicals (i.e. CF₃ CH₂ CH₂ --) and methyl radicals and a minor amount of vinyl radicals attached to silicon atoms in the backbone. Fluorosilicone polymers classified as "FVMQ" according to ASTM D-1418 are suitable. Commercially available fluorosilicone rubbers which can be used are sold under the trademark "Silastic", viz. "Silastic" LS 422, LS-420, and LS-53 and one sold as FSE-2120, all of which are silicone polymers having trifluoropropyl, methyl and vinyl substitutents attached to the silicon atoms--see Dow Corning Company bulletins 09-242, October, 1968, and 17-029, June 1971, and General Electric Company bulletin of February, 1978, on FSE-2120. The molecular weight of the fluorosilicone gums used as blend components in this invention can vary widely. Commercial fluorosilicone gums generally have a relatively low viscosity e.g. an inherent viscosity (0.2 g/deciliter in acetone at 25° C.) of about 0.1.

Any of the conventional "free-radical" generating cure initiators can be used in the vulcanization or curing of the fluoropolymer/fluorosilicone blend, such as actinic radiation, electron beam, and organic or inorganic peroxides; organic peroxides are preferred, particularly those which are stable at temperatures below about 50° C. and which decompose at a reasonable rate below about 200° C. Suitable peroxides include benzoyl peroxide, bis(2,4 dichlorobenzoyl) peroxide, dicumyl peroxide, 2,5-dimethyl-2,5-di(t-butylperoxy)hexane, t-butylhydroperoxide, di-t-butyl peroxide, t-butylperoxy benzoate, 2,5-dimethyl-2,5-di(t-butylperoxy)hexyne-3 and lauroyl peroxide. Particularly useful commercially available peroxides are 2,5-dimethyl-2,5-bis(t-butylperoxy)hexane and 2,5-dimethyl-2,5-bis(t-butylperoxy) hexyne-3 which are the active ingredients of products sold as "Luperco" 101XL and 130XL, respectively. The amount of peroxide curing agent used generally will be 0.1 to 5, preferably 1 to 2, parts per 100 parts of the fluoropolymer gum/fluorosilicone gum blend.

Along with the peroxide curing agent it will generally be desirable to use a cocuring agent (or coagent), such as are commonly used in peroxide vulcanization of rubbers to obtain a tighter or faster cure or better compression set. Such cocuring agents generally will be used in amounts of 1 to 10, preferably 1 to 5, parts per 100 parts of the fluoropolymer gum/fluorosilicone gum blend.

Cocuring agents which can be used include triallyl cyanurate, diallyl phthalate, allyl methacrylate and, particularly, triallyl isocyanurate.

In many cases, for optimum vulcanizate physical properties, such as tensile strength, it will be desirable to include in the blend finely divided silica as a reinforcing filler, e.g., 5 to 60 parts by weight per 100 parts by weight of the fluoropolymer/fluorosilicone admixture. The silica reinforcing fillers used for this purpose can be the same as those recommended by manufacturers of fluorosilicones as fillers therefor, such as those sold as "Cab-O-Sil" HS-5, "Aerosil" R-972, and "Quso" G-32.

In preparing the blend of this invention, it will usually be convenient to combine the fluoroelastomer gum and the silicone gum, then add the required or desired reinforcing fillers, such as silica, iron oxide, and zinc oxide, pigments, such as chrome oxide, iron oxide, and titanium oxide, acid acceptors, such as magnesium oxide and calcium hydroxide, plasticizers and processing aids which are compatible with the gums and mix well therewith, with the peroxide and cocuring agent (if used) being mixed in as the final step. For example, a two-roll mill can be used, preferably water-cooled to prevent the gumstock from scorching. The fluorocarbon polymer gum can be first banded on the mill and then the silicone gum blended in until uniform, or the two gums can be banded together. The balance of compounding adjuvants can then be milled in as a mixture. Generally, the compounded, vulcanizable mixture or gumstock is extruded or molded in a cavity or transfer mold at a temperature in the range of 125° to 250° C. for 1 to 50 minutes or more at about 5 to 10 MPa. The extruded or press-cured article is then transferred to a circulating air oven and post-cured at about 170° to 230° C. for about 2 to 24 hours, preferably at about 200° C. for 16 hours, yielding cured (that is, cross-linked or vulcanized) shaped articles which are elastomeric (i.e., materials which, when slowly stretched at room temperature to at least twice their original length and released, return rapidly to essentially their original length).

The vulcanizable blends of this invention can be employed in making molded or extruded articles of manufacture which are especially valuable in applications requiring performance over a broad temperature range, including those requiring high temperature stability and low temperature utility, such as gaskets, O-rings, diaphragms, tubing, ducting, carburetor fuel tips, fuel pump cups, shaft seals, and the like. The vulcanized blends are suitable in applications requiring high chemical resistance, such as conditions encountered by fabricated articles in aircraft hydraulic system seals, heat exchangers, pumps carburetors, and the like.

This invention provides a composite gumstock, at a relatively low cost, which can be vulcanized to elastomers with a TR₁₀ value sufficiently low to enable articles of such vulcanized elastomer to be used in low temperature environments, some types of these elastomers having TR₁₀ values of about -10° C. to -25° C. or lower, those having TR₁₀ values of about -20° C. to -25° C. being especially useful in automotive applications. These low temperature properties are coupled with good physical properties, initially and after exposure to elevated temperatures, resistance to aggressive fluids, and resistance to compression set. For example, as shown in the tables below, exemplary vulcanizates of this invention have TR₁₀ values of -10° C. or lower, many being lower than -20° C., and post-cured tensile strengths of at least about 7 MPa, most being above 9 MPa.

Objects and advantages of this invention are illustrated in the following examples, where the parts referred to are parts by weight unless indicated otherwise. The press-cured sheets, unless otherwise noted, were 150 mm×150 mm×2 mm sheets pressed at about 7 MPa for 15 minutes at 177° C. The post-cured sheets were those removed from the press and placed for 16 hours in a circulating air oven having a temperature maintained at 200° C. The accelerated aging was carried out according to ASTM D 573-67, the samples being exposed for the indicated time at the indicated temperature. Compression set was determined in accordance with ASTM D 395-69B using 15 mm diameter O-rings 3.5 mm thick compressed to 2.6 mm under the indicated conditions. Tensile strength, elongation at break, and modulus at 100 percent elongation were measured in accordance with ASTM D 412-75, using Die D. Hardness was measured in accordance with ASTM D 2240-75, using Durometer A and taking readings 2 seconds after the presser foot came into contact with the specimen. Volume swell was measured in accordance with ASTM-471-75, the change in volume after immersion in Reference Fuel C (equal volumes of isooctane and toluene), after 70 hours at 70° C., being measured in duplicate by the water displacement method. The TR₁₀ values, indicating utility at low temperature, were measured in accordance with ASTM D 1329-72 and are temperatures at which the specimen retracts 10% of its stretched length.

EXAMPLES

In accordance with this invention, a number of fluoropolymer gums (some of which were prepared as described above and some of which were obtained from commercial sources) were blended with commercially available fluorosilicone gums and certain compounding adjuvants, the resulting gumstocks were vulcanized, and the resulting vulcanizates were tested. For purposes of comparison, other gumstocks outside the scope of this invention were prepared, vulcanized, and tested. This work is summarized in the Tables I through V below, Table I setting forth the compositions of the fluoropolymers used, Table II setting forth the composition of the compounded gumstocks of this invention, Table III setting forth the composition of the comparison gumstocks, Table IV setting forth the properties of the vulcanized gumstocks of this invention, and Table V setting forth the properties of the comparison vulcanized gumstocks.

                                      TABLE I                                      __________________________________________________________________________                Composition, mol %                                                             VF.sub.2                                                                          HFP                                                                               C.sub.2 F.sub.3 Br                                                                  C.sub.2 HF.sub.2 Br                                                                 C.sub.2 HF.sub.3                                                                   C.sub.2 F.sub.4                                                                     C.sub.2 F.sub.3 OCF.sub.3                  __________________________________________________________________________     Fluoropolymer                                                                  gums used in                                                                   this invention                                                                 A          75.9                                                                              23.6                                                                              0.5                                                           B          78.4                                                                              21.3    0.3                                                      C          65.9                                                                              33.5                                                                              0.6                                                           D          67.0                                                                              32.6                                                                              0.4                                                           E          80.0                                                                              9.7                                                                               0.4       9.9                                                 F          78.1                                                                              20.1                                                                              1.8                                                           Comparison                                                                     Fluoropolymer gums                                                             G          55.4                                                                              24.2                                                                              1.4       19.0                                                H          76.1                                                                              20.0                                                                              3.9                                                           I          83.8                                                                              9.0                                                                               7.2                                                            J*        64.2                                                                              17.0                                                                              0.3           18.5                                             K*        53.9                                                                              19.6                                                                              0.4           26.1                                             L*        74.3                10.3 15.4                                        M*        74.2  0.5           7.7  17.6                                       __________________________________________________________________________      *These fluoropolymer gums were obtained commercially, gum L being              designated LD487.                                                        

                                      TABLE II                                     __________________________________________________________________________     Gumstock ingredients,                                                                      Gumstocks of Invention                                             parts       1  2  3  4  5  6  7  8  9  10 11                                   __________________________________________________________________________     Fluoropolymer gum                                                               A          60 60             80                                                B                60             80                                             C                   60                                                         D                      60          80                                          E                         60          80                                       F                                        80                                   Fluorosilicone gum.sup.a                                                                   40 40 40 40 40 40 20 20 20 20 20                                   Silica.sup.b                                                                               26.5                                                                              26.5                                                                              26.5                                                                              26.5                                                                              26.5                                                                              26.5                                                                              15 15 15 15 15                                   Iron oxide.sup.c              2.5                                                                               2.5                                                                               2.5                                                                               2.5                                                                               2.5                                  Calcium hydroxide                                                                          3  3  3  3  3  3                                                   Peroxide.sup.d                                                                             1.3                                                                               1.3                                                                               1.3                                                                               1.3                                                                               1.3                                                                               1.3                                                                               1.4                                                                               1.4                                                                               1.4                                                                               1.4                                                                               1.4                                  Triallyl isocyanurate                                                                      1.2                                                                               1.2                                                                               1.2                                                                               1.2                                                                               1.2                                                                               1.2                                                                               1.6                                                                               1.6                                                                               1.6                                                                               1.6                                                                               1.6                                  __________________________________________________________________________      .sup.a "Silastic" LS-420                                                       .sup.b Silica in gumstocks 1-6 was 20 parts "Aerosil" R972 and 6.5 parts       "CabO-Sil" HS-5, and in gumstocks 7-11 the silica was solely "Aerosil"         R972                                                                           .sup.c "Mapico" 297                                                            .sup.d Peroxide in gumstocks 1 and 3 was "Luperco" 101XL and in gumstocks      2, 4-11 it was "Luperco" 130XL                                           

                                      TABLE III                                    __________________________________________________________________________     Gumstock ingredients,                                                                     Comparison gumstocks                                                parts      12  13  14 15 16 17 18 19 20 21  22 23 24                           __________________________________________________________________________     Fluoropolymer                                                                   A         100                                                                  D             100                                                              G                 60                                                           J                    60             80                                         K                       60                                                     C                          80                                                  H                             80                                               I                                80                                            L                                          60                                  M                                             60 80                           Fluorosilicone gum.sup.a                                                                          40 40 40 20 20 20 20 100 40 40 20                           Silica.sup.b                                                                              26.5                                                                               26.5                                                                               26.5                                                                              26.5                                                                              26.5                                                                              15 15 15 15 26.5                                                                               26.5                                                                              26.5                                                                              15                           Iron oxide.sup.c            2.5                                                                               2.5                                                                               2.5                                                                               2.5          2.5                          Calcium hydroxide                                                                         3   3   3  3  3              3   3  3                               Peroxide.sup.d                                                                            1.3 1.3 1.3                                                                               1.3                                                                               1.3                                                                               1.4                                                                               1.4                                                                               1.4                                                                               1.4                                                                               1.3 1.3                                                                               1.3                                                                               1.4                          Triallyl isocyanurate                                                                     1.2 1.2 1.2                                                                               1.2                                                                               1.2                                                                               1.6                                                                               1.6                                                                               1.6                                                                               1.6                                                                               1.2 1.2                                                                               1.2                                                                               1.6                          __________________________________________________________________________      .sup.a "Silastic" LS-420                                                       .sup.b Silica in gumstocks 17-20 and 24 was "Aerosil" R972 and silica in       all other gumstocks was mixture of 20 parts "Aerosil" R972 and 6.5 parts       "CabO-Sil" HS-5                                                                .sup.c "Mapico" 297                                                            .sup.d "Luperco" 130XL                                                   

                                      TABLE IV                                     __________________________________________________________________________                  Vulcanizate products of invention***                                           1   2   3   4   5   6   7   8   9   10  11                        __________________________________________________________________________     Fluoropolymer gum used*                                                                     A   A   B   C   D   E   A   B   D   E   F                         FP/FS wt. ratio**                                                                           60/40                                                                              60/40                                                                              60/40                                                                              60/40                                                                              60/40                                                                              60/40                                                                              80/20                                                                              80/20                                                                              80/20                                                                              80/20                                                                              80/20                     Properties of vulcanizate:                                                     Press cure:                                                                    Tensile Strength, MPa                                                                       9.52                                                                               9.34                                                                               11.36                                                                              10.00                                                                              11.06                                                                              10.31                                                                              8.16                                                                               9.76                                                                               10.34                                                                              9.89                                                                               6.87                      Elongation, %                                                                               213 185 345 188 263 282 215 372 423 250 140                       100% modulus, MPa                                                                           4.14                                                                               5.16                                                                               3.30                                                                               5.85                                                                               4.93                                                                               4.10                                                                               3.07                                                                               3.50                                                                               2.24                                                                               4.07                                                                               5.49                      Hardness, Shore A                                                                           74  76  75  81  80  75  69  77  68  83  68                        Post cure:                                                                     Tensile strength, MPa                                                                       10.45                                                                              9.96                                                                               13.57                                                                              9.84                                                                               10.91                                                                              12.08                                                                              9.88                                                                               11.95                                                                              11.22                                                                              12.11                                                                              7.02                      Elongation, %                                                                               153 158 250 163 232 200 220 417 367 255 107                       100% modulus, MPa                                                                           5.96                                                                               6.38                                                                               4.70                                                                               6.14                                                                               5.22                                                                               5.41                                                                               3.53                                                                               3.42                                                                               2.68                                                                               3.74                                                                               6.53                      Hardness, Shore A                                                                           81  79  81  82  82  75  73  76  72  75  70                        Compression Set:                                                               70 hrs at 148° C.                                                                    --  17  --  29  26  22  20  25  21  22  23                        70 hrs at 200° C.                                                                    --  42  --  58  60  59  53  56  56  53  67                        TR.sub.10, °C.                                                                       -23.5                                                                              -23 -24 -10 -15 -21 -21 -22 -12 -14 -17                       Volume swell, vol. %                                                                        20  19  20  17  19  20  23  20  20  23  --                        Heat Aging:                                                                    3 days at 200° C.                                                       Tensile strength, MPa                                                                       --  9.22                                                                               --  10.09                                                                              10.82                                                                              11.31                                                                              8.91                                                                               13.07                                                                              10.13                                                                              10.14                                                                              5.21                      Elongation, %                                                                               --  150 --  160 225 182 227 463 358 245 122                       100% modulus, MPa                                                                           --  6.24                                                                               --  6.45                                                                               5.32                                                                               6.47                                                                               3.24                                                                               2.56                                                                               2.81                                                                               4.47                                                                               4.38                      Hardness, Shore A                                                                           --  80  --  81  81  82  70  63  71  82  66                        7 days at 200° C.                                                       Tensile strength, MPa                                                                       --  8.98                                                                               --  8.84                                                                               9.77                                                                               11.02                                                                              7.30                                                                               10.58                                                                              9.01                                                                               8.95                                                                               5.05                      Elongation, %                                                                               --  157 --  148 220 185 242 438 385 263 133                       100% modulus, MPa                                                                           --  5.80                                                                               --  6.31                                                                               4.84                                                                               6.05                                                                               2.61                                                                               2.39                                                                               2.47                                                                               3.62                                                                               3.91                      Hardness, Shore A                                                                           --  83  --  85  84  80  70  68  71  80  66                        14 days at 200° C.                                                      Tensile strength, MPa                                                                       --  7.39                                                                               --  7.53                                                                               9.20                                                                               9.05                                                                               6.90                                                                               8.39                                                                               7.86                                                                               8.24                                                                               5.74                      Elongation, %                                                                               --  142 --  137 222 163 272 453 398 277 137                       100% modulus, MPa                                                                           --  5.56                                                                               --  5.47                                                                               4.62                                                                               5.43                                                                               2.39                                                                               1.92                                                                               2.14                                                                               2.59                                                                               4.07                      Hardness, Shore A                                                                           --  83  --  84  84  80  68  69  70  69  71                        Heat aging:                                                                    3 days at 232° C.                                                       Tensile strength, MPa                                                                       --  8.03                                                                               --  7.56                                                                               9.18                                                                               8.38                                                                               5.64                                                                               8.03                                                                               6.19                                                                               6.41                                                                               4.62                      Elongation, %                                                                               --  165 --  165 238 160 288 493 453 290 133                       100% modulus, MPa                                                                           --  5.34                                                                               --  4.92                                                                               4.52                                                                               5.25                                                                               1.81                                                                               1.52                                                                               1.70                                                                               2.98                                                                               3.58                      Hardness, Shore A                                                                           --  78  --  84  79  80  65  62  66  78  72                        7 days at 232° C.                                                       Tensile Strength, MPa                                                                       --  5.43                                                                               --  4.25                                                                               5.81                                                                               5.05                                                                               5.25                                                                               7.19                                                                               5.24                                                                               6.05                                                                               5.18                      Elongation, %                                                                               --  163 --  148 243 148 332 543 503 315 122                       100% modulus MPa                                                                            --  3.90                                                                               --  3.21                                                                               3.13                                                                               3.23                                                                               1.66                                                                               1.30                                                                               1.52                                                                               2.48                                                                               4.56                      Hardness, Shore A                                                                           --  79  --  84  82  77  68  60  65  75  78                        14 days at 232° C.                                                      Tensile strength, MPa                                                                       --  3.17                                                                               --  3.15                                                                               3.03                                                                               3.34                                                                               6.17                                                                               7.39                                                                               5.45                                                                               5.61                                                                               3.91                      Elongation, %                                                                               --  168 --  117 238 168 340 548 533 302 78                        100% modulus, MPa                                                                           --  2.38                                                                               --  3.01                                                                               2.12                                                                               2.50                                                                               2.33                                                                               1.43                                                                               1.48                                                                               1.70                                                                               --                        Hardness, Shore A                                                                           --  80  --  82  80  76  76  68  67  66  77                        __________________________________________________________________________      *Fluoropolymer designations A,B, etc., correspond to those in Table I          **FP/FS means fluoropolymer gum/fluorosilicone gum ratio                       ***The numbered designations of the vulcanized products correspond to the      numbered designations of the gumstocks of Table II                       

                                      TABLE V                                      __________________________________________________________________________                Comparison vulcanizate products**                                              12  13  14  15  16  17  18  19  20  21  22  23  24                  __________________________________________________________________________     Fluoropolymer                                                                             A   D   G   J   K   C   H   I   J   None                                                                               L   M   M                   gum used*                                                                      FP/FS wt. ratio                                                                           100/0                                                                              100/0                                                                              60/40                                                                              60/40                                                                              60/40                                                                              80/20                                                                              80/20                                                                              80/20                                                                              80/20                                                                              0/100                                                                              60/40                                                                              60/40                                                                              80/20               Properties of                                                                  vulcanizate:                                                                   Press cure:                                                                    Tensile strength, MPa                                                                     12.91                                                                              14.42                                                                              6.30                                                                               5.10                                                                               5.73                                                                               8.51                                                                               5.32                                                                               3.23                                                                               6.07                                                                               6.09                                                                               6.68                                                                               10.18                                                                              11.22               Elongation, %                                                                             277 417 172 76  115 293 87  73  233 152 250 268 560                 100% modulus, MPa                                                                         4.56                                                                               4.36                                                                               3.25                                                                               --  --  2.35                                                                               --  --  3.13                                                                               3.67                                                                               4.44                                                                               4.40                                                                               2.01                Hardness, Shore A                                                                         76  87  73  83  77  69  67  65  73  62  78  78  64                  Post cure:                                                                     Tensile strength, MPa                                                                     14.08                                                                              17.90                                                                              6.13                                                                               6.56                                                                               5.50                                                                               9.99                                                                               3.73                                                                               2.98                                                                               5.92                                                                               4.87                                                                               8.87                                                                               10.66                                                                              12.53               Elongation, %                                                                             210 250 125 90  85  275 75  40  210 125 303 222 527                 100% modulus, MPa                                                                         5.98                                                                               7.01                                                                               4.53                                                                               --  --  2.88                                                                               --  --  3.50                                                                               3.62                                                                               4.62                                                                               5.20                                                                               2.01                Hardness, Shore A                                                                         79  87  76  85  80  73  71  72  77  63  80  80  65                  Compression Set:                                                               70 hrs at 148° C.                                                                  16  35  23  26  --  20  44  68  39  17  47  33  35                  70 hrs at 200° C.                                                                  35  64  51  50  --  63  100 --  78  68  73  69  74                  TR.sub.10, °C.                                                                     -19 -8  -11 -21 -14 -5  --  --  -17 -68 -35 -34 -33                 Volume swell, vol. %                                                                      17  17  23  18  --  20  --  --  18  27  20  21  27                  Heat Aging:                                                                    3 days at 200° C.                                                       Tensile strength, MPa                                                                     18.77                                                                              19.64                                                                              6.23                                                                               5.91                                                                               --  8.25                                                                               --  --  3.68                                                                               3.88                                                                               9.32                                                                               10.04                                                                              10.83               Elongation, %                                                                             255 227 112 65  --  258 --  --  203 115 372 200 523                 100% modulus, MPa                                                                         5.67                                                                               8.56                                                                               5.48                                                                               --  --  2.98                                                                               --  --  2.63                                                                               3.23                                                                               4.84                                                                               5.21                                                                               2.02                Hardness, Shore A                                                                         82  91  78  85  --  71  --  --  74  61  75  80  64                  7 days at 200° C.                                                       Tensile strength, MPa                                                                     16.54                                                                              18.44                                                                              6.35                                                                               5.96                                                                               --  7.23                                                                               --  --  3.45                                                                               3.65                                                                               8.79                                                                               9.40                                                                               9.45                Elongation, %                                                                             215 237 117 77  --  270 --  --  227 128 297 208 548                 100% modulus, MPa                                                                         6.12                                                                               7.85                                                                               5.22                                                                               --  --  2.60                                                                               --  --  2.35                                                                               2.62                                                                               4.40                                                                               4.83                                                                               1.79                Hardness, shore A                                                                         81  87  77  87  --  70  --  --  76  61  81  81  63                  14 days at 200° C.                                                      Tensile strength, MPa                                                                     18.31                                                                              18.37                                                                              5.27                                                                               5.64                                                                               --  6.72                                                                               --  --  2.99                                                                               3.44                                                                               7.92                                                                               7.36                                                                               8.61                Elongation, %                                                                             247 255 107 78  --  277 --  --  250 117 312 180 605                 100% modulus, MPa                                                                         5.56                                                                               7.02                                                                               4.89                                                                               --  --  2.38                                                                               --  --  1.96                                                                               2.72                                                                               3.80                                                                               4.46                                                                               1.52                Hardness, Shore A                                                                         80  88  78  87  --  69  --  --  77  60  80  81  63                  Heat aging:                                                                    3 days at 232° C.                                                       Tensile strength, MPa                                                                     12.37                                                                              19.75                                                                              4.09                                                                               5.53                                                                               --  5.01                                                                               --  --  2.52                                                                               2.60                                                                               7.52                                                                               7.89                                                                               6.86                Elongation, %                                                                             313 312 93  83  --  290 --  --  270 128 312 218 647                 100% modulus, MPa                                                                         3.40                                                                               6.57                                                                               --  --  --  2.01                                                                               --  --  1.85                                                                               1.99                                                                               3.99                                                                               4.07                                                                               1.25                Hardness, Shore A                                                                         77  90  77  86  --  67  --  --  74  58  78  82  60                  7 days at 232° C.                                                       Tensile strength, MPa                                                                     11.23                                                                              11.98                                                                              2.15                                                                               4.41                                                                               --  5.38                                                                               --  --  3.07                                                                               2.11                                                                               4.91                                                                               4.72                                                                               5.65                Elongation, %                                                                             412 390 68  78  --  335 --  --  347 113 357 240 673                 100% modulus MPa                                                                          2.44                                                                               3.84                                                                               --  --  --  2.25                                                                               --  --  1.99                                                                               1.92                                                                               2.72                                                                               2.76                                                                               1.17                Hardness, Shore A                                                                         77  87  73  86  --  71  --  --  76  58  78  79  60                  14 days at 232° C.                                                      Tensile strength, MPa                                                                     8.66                                                                               10.94                                                                              1.79                                                                               2.50                                                                               --  5.12                                                                               --  --  4.28                                                                               2.25                                                                               2.52                                                                               2.60                                                                               5.05                Elongation, %                                                                             400 440 60  25  --  293 --  --  418 95  408 258 603                 100% modulus, MPa                                                                         2.36                                                                               3.38                                                                               --  --  --  2.51                                                                               --  --  2.01                                                                               --  1.82                                                                               1.97                                                                               1.23                Hardness, Shore A                                                                         79  86  76  84  --  79  --  --  78  61  75  75  66                  __________________________________________________________________________      *Fluoropolymer designations A, B, etc., correspond to those in Table I         **The numbered designations of the vulcanized products correspond to the       numbered designations of the gumstocks of Table III                      

To illustrate further aspects of this invention, in a series of seven runs, fluoropolymer A (whose composition is set forth in Table I) was blended with varying amounts of fluorosilicone gum and various other compounding adjuvants, the blends were press-cured at 177° C. for 15 minutes at 5 MPa, post-cured at 200° C. for 16 hours, heat aged for different periods of time at 200° C. and 232° C. and the properties of the various cured and aged vulcanizates were determined. These runs are summarized in Table VI.

                                      TABLE V                                      __________________________________________________________________________                     25 26  27  28  29  30  31                                      __________________________________________________________________________     Gumstock ingredients, parts:                                                   Fluoropolymer gum A                                                                           20  40  85  90  80  60  60                                      Fluorosilicone gum.sup.a                                                                      80  60  15  10  20  40  40                                      Silica.sup.b   26.5                                                                               26.5                                                                               20  20  15  26.5                                        Iron Oxide.sup.c               2.5     60.sup.f                                Calcium hydroxide 3                                                                           3   3   3       3   3                                           Peroxide.sup.d 1.3 1.3 1.3 1.3 1.3 1.3 2                                       Triallyl isocyanurate                                                                         1.2 1.2 1.2 1.2         2                                       Properties of vulcanizate:                                                     Press cure.sup.e :                                                             Tensile strength, MPa                                                                         6.95                                                                               8.29                                                                               9.67                                                                               11.19                                                                              7.65                                                                               7.94                                                                               5.87                                    Elongation, %  160 178 217 205 498 333 160                                     100% modulus, MPa                                                                             3.99                                                                               4.26                                                                               3.53                                                                               4.48                                                                               1.18                                                                               2.28                                                                               3.88                                    Hardness, Shore A                                                                             70  74  67  73  53  70  65                                      Post cure.sup.e :                                                              Tensile strength, MPa                                                                         6.85                                                                               7.61                                                                               12.93                                                                              13.99                                                                              9.14                                                                               9.29                                                                               7.05                                    Elongation, %  150 152 200 180 443 247 110                                     100% modulus, MPa                                                                             4.16                                                                               4.72                                                                               4.92                                                                               6.20                                                                               1.64                                                                               3.79                                                                               6.23                                    Hardness, Shore A                                                                             72  76  70  77  58  75  67                                      Compression set:                                                               70 hrs at 148° C.                                                                      9   11  --  --  24  23  --                                      70 hrs at 200° C.                                                                      36  35  --  --  64  60  --                                      TR.sub.10, °C.                                                                         -52 -29 -20 -20 -21 -23 --                                      Volume, Swell, vol. %                                                                         24  23  19  18  24  25  --                                      Heat Aging:                                                                    3 days at 200° C.                                                       Tensile strength, MPa                                                                         5.80                                                                               5.45                                                                               --  --  8.78                                                                               9.13                                                                               --                                      Elongation, %  147 127 --  --  440 240 --                                      100% modulus, MPa                                                                             3.48                                                                               4.21                                                                               --  --  1.77                                                                               4.02                                                                               --                                      Hardness, Shore A                                                                             72  78  --  --  58  77  --                                      7 days at 200° C.                                                       Tensile strength, MPa                                                                         5.72                                                                               6.00                                                                               --  --  7.38                                                                               8.72                                                                               --                                      Elongation, %  150 123 --  --  460 217 --                                      100% modulus, MPa                                                                             3.40                                                                               4.59                                                                               --  --  1.73                                                                               4.39                                                                               --                                      Hardness, Shore A                                                                             71  79  --  --  58  79  --                                      14 days at 200° C.                                                      Tensile strength, MPa                                                                         4.86                                                                               5.90                                                                               --  --  5.02                                                                               5.05                                                                               --                                      Elongation, %  135 135 --  --  420 210 --                                      100% modulus, MPa                                                                             3.39                                                                               4.27                                                                               --  --  1.23                                                                               3.94                                                                               --                                      Hardness, Shore A                                                                             71  78  --  --  58  76  --                                      __________________________________________________________________________                    Runs                                                                           25  26  27  28  29  30  31                                      __________________________________________________________________________     Heat aging:                                                                    3 days at 232° C.                                                       Tensile strength, MPa                                                                         4.34                                                                               5.23                                                                               --  --  4.85                                                                               7.58                                                                               --                                      Elongation, %  152 138 --  --  174 243 --                                      100% modulus, MPa                                                                             2.72                                                                               4.01                                                                               --  --  3.56                                                                               3.69                                                                               --                                      Hardness, Shore A                                                                             69  77  --  --  58  76  --                                      7 days at 232° C.                                                       Tensile strength, MPa                                                                         3.30                                                                               3.94                                                                               --  --  5.58                                                                               6.61                                                                               --                                      Elongation, %  153 135 --  --  573 220 --                                      100% modulus, MPa                                                                             2.17                                                                               3.03                                                                               --  --  1.32                                                                               3.72                                                                               --                                      Hardness, Shore A                                                                             68  77  --  --  58  78  --                                      14 days at 232° C.                                                      Tensile strength, MPa                                                                         1.36                                                                               1.90                                                                               --  --  5.61                                                                               4.27                                                                               --                                      Elongation, %  122 103 --  --  563 327 --                                      100% modulus, MPa                                                                             1.27                                                                               1.84                                                                               --  --  1.14                                                                               2.52                                                                               --                                      Hardness, Shore A                                                                             65  75  --  --  61  74  --                                      __________________________________________________________________________      .sup.a "Silastic" LS-420                                                       .sup.b Silica used in runs 25, 26 and 30 was 20 parts "Aerosil" R972 and       6.5 parts "CabO-Sil" HS-5, in runs 27 and 28 it was "Quso" G32, in run 29      it was "Aerosil" R972                                                          .sup.c "Mapico" 297                                                            .sup.d "Luperco" 130XL in runs 25, 26, 29, and 30 and "Luperco" 101XL in       runs 27,28, and 31                                                             .sup.e Values for runs 25-2 are average of two determinations                  .sup.f This 60 parts was a "Mapico Tan" 10, a mixture of 67% iron oxide        and 33% zinc oxide                                                       

Various modifications and alterations of this invention will be apparent to those skilled in the art without departing from the scope and spirit of this invention and the latter should not be restricted to that set forth herein for illustrative purposes. 

What is claimed is:
 1. A composition comprising a blend of (a) 90 to 20 parts by weight fluoropolymer gum whose interpolymerized units consist essentially of 60 to 85 mol percent of units derived from vinylidene fluoride, 10 to 40 mol percent of units derived from hexafluoropropene, and 0.15 to 3 mol percent of units derived from bromine-containing copolymerizable olefin, and (b) 10 to 80 parts by weight fluorosilicone gum, said parts by weight being based on 100 parts by weight of the sum of the weights of said gums, both of which gums cure in the presence of free-radical initiators under vulcanization conditions to produce an elastomeric vulcanizate.
 2. A vulcanizable composition vulcanizable to an elastomeric vulcanizate, said composition comprising a blend of (a) 90 to 20 parts by weight fluoropolymer gum whose interpolymerized units consist essentially of 60 to 85 mol percent of units derived from vinylidene fluoride, 10 to 40 mol percent of units derived from hexafluoropropene, and 0.15 to 3 mol percent of units derived from bromine-containing copolymerizable olefin having 2 to 4 carbon atoms, and (b) 10 to 80 parts by weight fluorosilicone gum which contains trifluoropropyl radicals attached to silicon atoms, said parts by weight being based on 100 parts by weight of the sum of the weights of said gums, both of which gums cure in the presence of free-radical initiators under vulcanization conditions to produce an elastomeric vulcanizate.
 3. The vulcanizable composition according to claim 2 wherein said bromine-containing olefin is bromotrifluoroethylene.
 4. The vulcanizable composition according to claim 2 wherein said bromine-containing olefin is 1-bromo-2,2-difluoroethylene.
 5. The vulcanizable composition according to claim 2 wherein said fluoropolymer gum has interpolymerized units consisting of 65 to 82 mol percent units derived from vinylidene fluoride, 17 to 35 mol percent of units derived from hexafluoropropene, and 0.2 to 0.6 mol percent units derived from said bromine-containing olefin.
 6. The vulcanizable composition of claim 2 further comprising 5 to 60 parts by weight of reinforcing silica filler per 100 parts by weight of the sum of the weights of said gums.
 7. The vulcanizable composition of claim 2 further comprising an organic peroxide free-radical initiator as a curing agent.
 8. The vulcanizable composition of claim 2 further comprising 2,5-dimethyl-2,5-bis(t-butylperoxy) hexane or 2,5-dimethyl-2,5-bis(t-butylperoxy)hexyne-3 as a vulcanizing agent.
 9. The vulcanizable composition of claim 2 further comprising triallyl isocyanurate as a cocuring agent.
 10. A vulcanizable gumstock comprising a blend of (a) 60 to 90 parts by weight of elastomeric fluoropolymer gum whose interpolymerized units consist essentially of 60 to 85 mol percent of units derived from vinylidene fluoride, 10 to 40 mol percent of units derived from hexafluoropropene, and 0.15 to 3 mol percent of units derived from bromotrifluoroethylene or 1-bromo-2,2-difluoroethylene, (b) 40 to 10 parts by weight of methyl vinyl trifluoropropyl silicone gum (c) 5 to 60 parts by weight silica reinforcing filler, (d) 2,5-dimethyl-2,5-bis(t-butylperoxy)hexane or 2,5-dimethyl-2,5-bis(t-butylperoxy)hexyne-3 as a curing agent for both of said gums, and (e) triallyl isocyanurate as a cocuring agent, said parts by weight being based on 100 parts by weight of the sum of the weights of said gums, said gumstock upon being vulcanized yielding an elastomer having a post-cured tensile strength of at least 7 MPa and a TR₁₀ value in the range of -10° to -25° C.
 11. A process for making an elastomeric shaped article, comprising extruding or molding the vulcanizable composition of claim 2, and curing the resulting shaped article.
 12. A shaped article made according to claim
 11. 